Analog 5-wire PET-On-Glass Touch Screen Specification
1. Mechanical Dimensions and Construction 1.1 General: Analog Resistive touch screen is laminated by ITO PET to ITO glass. 1.2 Construction : Item 1 2 3 4 5 6 7 8 9 10 Material Remarks 0.188mm ITO PET Film Antiglare coating Surface hardness: 3H Resistance:300~600/ ITO Patterned Glass (Bottom 2,85mm ITO Glass Resistance:300~600/ layer) Tail Base Kapton Separated Tail Tail cover lay Kapton Connector AMP Compatible Pitch:2.54mm Top layer circuit Silver ink Bottom layer circuit Silver ink Layer to layer contacted Silver ink Dot spacer UV Cure ink Isolation Layer Isolation Adhesive Description ITO PET (Top layer)
Touch screen side view:
Changes that contribute to technical improvement are subject to alternations
2004 Bearb. Gepr. Vert.
Datum 22.07. 22.07.
Name Maurer Maurer
TOUCH SCREEN
17,1", 5-Wire
AMT-02505-01 SPECIFICATIONS OF ANALOG RESISTIVE PET-ON-GLASS TOUCH SCREEN Manufactured by Apex Material Technology Corp.
EDV-Datasheet
don't change manually
H
Zu And. Datum Name
1070.0453
Index: -
D 79346 Endingen
Blatt 1 von 4
1.3 Input Method and Activation Force Input Method 16mm dia. Silicon "finger" Average Activation Force Less than 1.00 N
2. Typical Optical Characteristics 2.1 2.2 Visible Light Transmission: >80% Haze: <12%
3. Electrical Specifications 3.1 3.2 3.3 3.4 3.5 3.6 Operating Voltage: Contact current: Circuit close resistance: Circuit open resistance: Contact bounce: Linearity Specifications: 5.5V or less 20mA (maximum) 20~300 > 10M at 25VDC < 15ms The linearity specifications are based on Hampshire or PenMount touch screen controllers and drivers to define. 10 mm inside of X and Y active area dimensions. The area 10 mm inside of X and Y active area dimensions.
3.6.1 Inner Active Area : Perimeter of Active Area :
Changes that contribute to technical improvement are subject to alternations
2004 Bearb. Gepr. Vert.
Datum 22.07. 22.07.
Name Maurer Maurer
TOUCH SCREEN
17,1", 5-Wire
AMT-02505-01 SPECIFICATIONS OF ANALOG RESISTIVE PET-ON-GLASS TOUCH SCREEN Manufactured by Apex Material Technology Corp.
EDV-Datasheet
don't change manually
H
Zu And. Datum Name
1070.0453
Index: -
D 79346 Endingen
Blatt 2 von 4
3.6.2 Calculate Linearity
% Linearity =
X 2 + Y 2 * 100 Active Area Diagonal
G Y G X
3.6.3 Linearity : Inner Active Area : <1.0% Perimeter of Active Area : <2.0%
4. Environment Specification 4.1 4.2 Operating Temperature - 10 C ~ + 50 C Humidity less than 80% RH Storage Temperature - 40 C ~ + 80 C at Ambient Humidity
5. Reliability Test 5.1 Exposure to high temperature Touch panel is put into a test machine at the condition of 80 for 120 hours. Then it is left at the room temperature for 24 hours or more. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6
Changes that contribute to technical improvement are subject to alternations
2004 Bearb. Gepr. Vert.
Datum 22.07. 22.07.
Name Maurer Maurer
TOUCH SCREEN
17,1", 5-Wire
AMT-02505-01 SPECIFICATIONS OF ANALOG RESISTIVE PET-ON-GLASS TOUCH SCREEN Manufactured by Apex Material Technology Corp.
EDV-Datasheet
don't change manually
H
Zu And. Datum Name
1070.0453
Index: -
D 79346 Endingen
Blatt 3 von 4
5.2
Exposure to low temperature Touch panel is put into a test machine at the condition of -40C for 120 hours. Then it is left at the room temperature for 24 hours or more. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6 Exposure to constant temperature and humidity Touch panel is put into a test machine at the condition of 50C, 80%RH for 120 hours. Then it is left at the room temperature for 24 hours or more. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6 Thermal Shock Touch panel is put into a test machine at the condition of -40C for 30 minutes, and then 80C for 30 minutes. The process is repeated by 10 cycles. Then it is left at the room temperature for 24 hours or more. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6
5.3
5.4
6. Durability test: 6.1 Finger touches Touch panel is hit 36 millions times with a silicone rubber of R8 finger, hitting rate is by 250g at 2 times per second. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6
7. Optical Performance: 7.1 7.2 7.3 7.4 Optical inspection method and optical defect refer to document Touch Screen Optical Quality Standard. Outside to Active Area : any optical defected in this area need to be ignored if no effected to touch screen function. Glass defects such as edge chips and scratches refer to Touch Screen Optical Quality Standard. Others: Always store the touch screen in its original shipping container under normal conditions (20~25C, 65% RH)
Changes that contribute to technical improvement are subject to alternations
2004 Bearb. Gepr. Vert.
Datum 22.07. 22.07.
Name Maurer Maurer
TOUCH SCREEN
17,1", 5-Wire
AMT-02505-01 SPECIFICATIONS OF ANALOG RESISTIVE PET-ON-GLASS TOUCH SCREEN Manufactured by Apex Material Technology Corp.
EDV-Datasheet
don't change manually
H
Zu And. Datum Name
1070.0453
Index: -
D 79346 Endingen
Blatt 4 von 4

▲Up To Search▲

Price & Availability of 10700453

	To Download 10700453 Datasheet File
If you can't view the Datasheet, Please click here to try to view without PDF Reader .